Chantal Pia Lorbeer

• The dissertation at hand aims at contributing to the elucidation of size-property and structure-property relationships of inorganic luminescent materials. In detail, fluoridic nanomaterials with an average particle size of 5-20 nm were characterized and optimized with regard to their light converting potential. By using a simple microwave-assisted synthesis method based on task-specific ionic liquids, quantum cutting materials for the conversion of vacuum ultraviolet radiation have been prepared. A quantum cutting efficiency close to the theoretical limit was achieved. In a second step, white light emitting nanoparticles close to standard daylight were successfully synthesized. Finally, an approach to the substitution of rare earths has been developed and tested. The emerging charge compensation problems have been studied by a multi-analytical approach.
• Die vorliegende Arbeit stellt einen Beitrag zur Erforschung des Partikelgrößen- und Struktureffektes anorganischer Leuchtstoffe auf ihre Materialeigenschaften dar. Hierbei wurden insbesondere fluoridische Nanomaterialien mit einer durchschnittlichen Partikelgröße von 5-20 nm hinsichtlich potentieller lichtkonvertierender Anwendungen untersucht und optimiert. Mittels einer einfachen Synthese unter Anwendung von Mikrowellenstrahlung und funktionalen ionischen Flüssigkeiten wurden zunächst \(\textit {Quantum-Cutting}\) Materialien für den vakuumultravioletten Bereich dargestellt und charakterisiert. Hierbei konnte eine Quanteneffizienz nahe der theoretischen Grenze erreicht werden. In einem zweiten Schritt wurden erfolgreich nanoskalige Leuchtstoffe entwickelt, die weißes Licht, ähnlich dem Tageslicht, emittieren. Im letzten Schritt wurde dann ein Ansatz zur Substitution seltener Erden in den Materialien entwickelt und die dabei auftretenden Ladungskompensationsprobleme multianalytisch untersucht.