Avinash Hariharan

• In the additive manufacturing of polycrystalline nickel-base superalloy Inconel-738LC (IN738LC) by laser-powder bed fusion (L-PBF), the critical issue is the formation of micro-cracks during the process. These are solidification cracks that occur at the last stage of solidification. The first part of the thesis is an extensive chemical composition analysis at high-angle and low-angle grain boundaries with solidification cracks and on those that are devoid of cracks. The second part of the thesis consists of a multi-scale residual stress study. These results are used to rationalize the contribution of solute enrichment and tensile stresses at interfaces to the solidification cracking mechanism during the L-PBF process.
• Bei der additiven Herstellung der polykristallinen Superlegierung auf Nickelbasis Inconel-738LC (IN738LC) durch Laser-Pulverbett-Schmelzen (L-PBF) ist eines der Hauptprobleme die Ausbildung von Mikrorissen während des Prozesses. Dabei handelt es sich um Erstarrungsrisse, die in der letzten Phase der Erstarrung entstehen. Der erste Teil der Arbeit ist eine umfassende Analyse der chemischen Zusammensetzung an Groβ- und Kleinwinkelkorngrenzen mit Erstarrungsrissen und an solchen, die frei von Rissen sind. Der zweite Teil der Arbeit besteht aus einer mehrskaligen Eigenspannungsanalyse. Diese Ergebnisse werden verwendet, um die Beiträge der Segregation gelöster Atome und der Zugspannungen an Grenzflächen zum Erstarrungsrissmechanismus während des L-PBF-Prozesses aufzuklären.